我叫周若男，是中科院宁波材料所海洋实验室与宁波诺丁汉大学联合培养2023级博士研究生，主要从事相图计算、多组元合金涂层的设计制备与服役性能探究，以及机理探索。

该论文《Effect of molybdenum addition on oxidation behavior and secondary protection mechanism of FeCrAl coatings》发表于Materials Characterization，中科院JCR分区为一区Top期刊，影响因子4.7。在文章我们使用了贝意克的真空管式炉设备，论文原文如下：The oxidation tests were conducted in a horizontal tube furnace (BTF–1200C, BEQ Company, China) at 550 ℃ in air. The specimens were placed into the center of the furnace when the temperature stabilized and were oxidized for 10 min, 30 min, and 120 min, respectively. After the oxidation test, the specimens were directly taken out from the furnace and cooled down to room temperature in laboratory air. Before examining the cross-sectional morphologies, the oxidized specimens were encapsulated using epoxy glue and polished using abrasive papers.

文中所用到的设备正是安徽贝意克设备技术有限公司生产的BTF-1200C真空管式炉，我们使用该设备对我的样品下进行了550 ℃进行了氧化，氧化时间10min/30min/120min。贝意克设备具有良好的热稳定性、精准的温控和良好的保温效果，助力我们完成氧化实验。该设备购买于2018年，已在实验室服役5年，但设备性能依旧满足我们日常的实验，中间有过一次保外维修，贝意克的工程师给予我们很宝贵的指导，为我们科研的顺利提供了关键的保障，在此表示感谢，也祝愿安徽贝意克公司能够越办越好，更上一层楼！