SiO2/Al2O3

mol/mol

150

Na2O Content

wt%

0.04

Crystal Size 

μm

0.2-0.4

BET Surface Area 

 m2/g

380

Pore Size 

nm

0.54

Bulk density

Kg/m³

500

X-ray Crystallinity

%

95

Pore Capacity

ml/g

>0.21

Lattice constant (nm)

Å

24.10

Ignition Loss（550℃ 3h）

wt%

<8

Water Adsorption at 50% EH and 20FC

wt%

5